RESEARCH OF CATHODE PROCESS AT CORROSION STANDARDS, PROTECTED BY POLYMERIC TAPES, IN SOLUTION OF NACL
Rubrics: CHEMISTRY AND CHEMICAL TECHNOLOGY
Authors:
Type:
Article
Pages:
from 107
to 108
Status:
Published
Received:
11.05.2021
Accepted:
10.01.2022
Published:
10.01.2022
Subject area:
GRNTI 31.01 Общие вопросы химии
Language:
Russian
Keywords:
corrosion, cathode reaction, polarization, oxygen, renewal
Abstract (English):
A corrosion study of ST-3 steel samples in a 3% sodium chloride solution was carried out. The test steel samples were pre-coated with two different polymer films based on styreneacrylic latexes. The analysis of the process of cathodic polarization shows that on the metal in both.
A corrosion study of ST-3 steel samples in a 3% sodium chloride solution was carried out. The test steel samples were pre-coated with two different polymer films based on styreneacrylic latexes. The analysis of the process of cathodic polarization shows that on the metal in both.
Keywords:
corrosion, cathode reaction, polarization, oxygen, renewal
corrosion, cathode reaction, polarization, oxygen, renewal
1. Rozelfel'd I.L., Rubinshteyn F.I., Zhigalova K.A. Zaschita metallov ot korrozii lakokrasochnymi pokrytiyami. M.: Himiya, 1987. S. 224.
2. Shinkareva E.V., Koshevar V.D. Antikorrozionnaya gruntovka na osnove vodnoy epoksidnoy emul'sii i uglerodnyh nanochastic // ZhPH. 2016. t. 89, № 1. S. 68-76.
3. Yakovleva A.A., Anciferov E.A., Guseva E.A., Sadlovskiy S.V. Vliyanie zaschitnogo pokrytiya na osnove organicheskogo svyazuyuschego na korrozionnuyu ustoychivost' stali // Izvestiya vuzov. Prikladnaya himiya i biotehnologiya. 2019.